HEAT SHRINKABLE CABLE FEED-THROUGHS
Features/Applications
QCFT is made from radiation cross-linked polyolefin. It is suitable for
applications in moisture and pressure proof sealing of plastic and metal
parts. It can also be used in sealing vacant cable duct and protecting pipes.
Technical Data
MOLDED PARTS Qualtek Electronics
Typical DataProperty
Test Method
Operating Temperature
Tensile Strength
Tensile Strength After Thermal Aging (120°C, 168 hrs.)
Elongation at Break
Elongation at Break After Thermal Aging (120°C, 168 hrs.)
Dielectric Strength
Volume Resistance
Water Absorption
13
-55°C to +110°C
13 MPa min.
10 MPa min.
300% min.
250% min.
15kV / mm (min.)
10 Ω.cm (min.)
1% max.
IEC 216
ASTM D 2671
ASTM D 2671
ASTM D 2671
ASTM D 2671
IEC 243
IEC 93
ISO 62
QCFT 110 (85/42-15/5)
QCFT 120 (60/30-45/10)
QCFT 130 (100/52-20/8)
QCFT 130L (100/50-20/8)
QCFT 135 (150/92-14/5)
QCFT 140 (160/92-60/20)
QCFT 150 (160/92-100/45)
85
60
100
100
150
160
160
2.5
2.5
3.0
3.0
3.5
3.2
3.5
15
45
20
20
14
60
100
5
10
8
8
5
20
45
130
130
150
210
150
150
150
45
45
65
70
55
50
50
2.8
4.5
3.0
3.0
3.5
3.0
3.5
l (mm)
a (Min.) L (mm)
Recovered Length
± 10%
Recovered Wall
± 10%
Product Dimensions
Part
Number
a (Min.)
b (Max.)
D (mm)
b (Max.) F (mm) Dw (mm) lw(mm)
42
30
52
50
92
92
92
Notes:
(a) as supplied
(b) after recovery
Operating temperature: -55°C to +110°C
Minimum shrink temperature: 110°C
Standard color: Black
RoHS Compliant
Applicable pressure up to 1 bar
Easy to install
Resistant against chemical and UV
ISO-9001 Company
www.qualtekusa.com
QCFT-200C