▶ This catalog contains the typical specification only due to the limitation of space. When you consider the purchase of our products, please check our specification.
For details of each product (characteristics graph, reliability information, precautions for use, and so on), see our Web site (http://www.ty-top.com/) .
c_mlcc_reli_e-E02R01
13. Resistance to Soldering
Specified
Value
Temperature
Compensating(Class1)
Standard
Appearance : No abnormality
Capacitance change : Within ±2.5% or ±0.25pF, whichever is larger.
Q : Initial value
Insulation resistance : Initial value
Withstanding voltage (between terminals) : No abnormality
High Frequency Type
Appearance : No abnormality
Capacitance change : Within ±2.5%
Q : Initial value
Insulation resistance : Initial value
Withstanding voltage (between terminals) : No abnormality
High Permittivity (Class2) Note 1
Appearance : No abnormality
Capacitance change : Within ±7.5%(BJ, B7, C6, C7, LD(※))
Within ±20%(F)
Dissipation factor : Initial value
Insulation resistance : Initial value
Withstanding voltage (between terminals): No abnormality
Note: ※LD Low distortion high value multilayer ceramic capacitor
Test
Methods and
Remarks
Class 1
042, 063 Type 105 Type
Preconditioning None
Preheating 150℃, 1 to 2 min.
80 to 100℃, 2 to 5 min.
150 to 200℃, 2 to 5 min.
Solder temp. 270±5℃
Duration 3±0.5 sec.
Recovery 6 to 24 hrs (Standard condition) Note 5
Class 2
042、063 Type 105, 107, 212 Type 316, 325 Type
Preconditioning Thermal treatment (at 150℃ for 1 hr) Note 2
Preheating 150℃, 1 to 2 min.
80 to 100℃, 2 to 5 min.
150 to 200℃, 2 to 5 min.
80 to 100℃, 5 to 10 min.
150 to 200℃, 5 to 10 min.
Solder temp. 270±5℃
Duration 3±0.5 sec.
Recovery 24±2 hrs (Standard condition) Note 5
14. Temperature Cycle (Thermal Shock)
Specified
Value
Temperature
Compensating(Class1)
Standard
Appearance : No abnormality
Capacitance change : Within ±2.5% or ±0.25pF, whichever is larger.
Q : Initial value
Insulation resistance : Initial value
Withstanding voltage (between terminals) : No abnormality
High Frequency Type
Appearance : No abnormality
Capacitance change : Within ±0.25pF
Q : Initial value
Insulation resistance : Initial value
Withstanding voltage (between terminals) : No abnormality
High Permittivity (Class2) Note 1
Appearance : No abnormality
Capacitance change : Within ±7.5% (BJ, B7, C6, C7, LD(※))
Within ±20% (F)
Dissipation factor : Initial value
Insulation resistance : Initial value
Withstanding voltage (between terminals) : No abnormality
Note: ※LD Low distortion high value multilayer ceramic capacitor
Test
Methods and
Remarks
Class 1 Class 2
Preconditioning None
Thermal treatment (at 150℃ for 1 hr)
Note 2
1 cycle
Step Temperature(℃) Time(min.)
1 Minimum operating temperature 30±3
2 Normal temperature 2 to 3
3 Maximum operating temperature 30±3
4 Normal temperature 2 to 3
Number of cycles 5 times
Recovery 6 to 24 hrs (Standard condition) Note 5 24±2 hrs (Standard condition) Note 5