AC0805CKX7R9BB

AC0805CKX7R9BB首页预览图
型号: AC0805CKX7R9BB
PDF文件:
  • AC0805CKX7R9BB PDF在线浏览
功能描述: SURFACE MOUNT MULTILAYER CERAMIC CAPACITORS
PDF文件大小: 1763.89 Kbytes
PDF页数: 共24页
制造商: YAGEO[YAGEO Corporation]
制造商LOGO: YAGEO[YAGEO Corporation] LOGO
制造商网址: http://www.yageo.com
捡单宝
PDF页面索引
100%
Automotive grade
NP0/X7R
6.3 V to 630 V
www.yageo.com
Mar. 31, 2017 V.6
Surface-Mount Ceramic Multilayer Capacitors
19
24
Product specification
TEST
TEST METHOD
PROCEDURE
REQUIREMENTS
Operational Life
AEC-Q200
8
1. Preconditioning, class 2 only:
150 +0/-10 °C /1 hour, then keep for
24 ± 1 hour at room temp
2. Initial measure:
Spec: refer to initial spec C, D, IR
3. Endurance test:
Temperature: X7R: 125 °C
Specified stress voltage applied for 1,000 hours:
Applied 2.0 x U
r
for general products
Applied 1.5 x U
r
for high cap. Products
High voltage series follows with below
stress condition:
Applied 1.5 x Ur for 200V, 250V series
Applied 1.3 x Ur for 500V, 630V series
Applied 1.2 x Ur for 1KV, 2KV, 3KV series
4. Recovery time: 24 ± 2 hours
5. Final measure: C, D, IR
Note: If the capacitance value is less than the minimum value
permitted, then after the other measurements have been
made the capacitor shall be preconditioned according to “IEC
60384 4.1” and then the requirement shall be met.
No visual damage
C/C
NP0: Within ± 2% or 1 pF,
whichever is greater
X7R: ± 15%
D.F.
NP0: 2 x specified value.
X7R: 16V: 7%
25V: 5%
IR
NP0: 4,000 MΩ or IR x C
r
40s whichever is less
X7R: 1,000 MΩ or IRx C
r
50s whichever is less
External Visual
AEC-Q200
9
Any applicable method using × 10 magnification
In accordance with
specification
Physical
Dimension
AEC-Q200
10
Verify physical dimensions to the applicable device
specification.
In accordance with
specification
Mechanical
Shock
AEC-Q200
13
Three shocks in each direction shall be applied along the three
mutually perpendicular axes of the test specimen (18 shocks)
Peak value: 1,500 gs
Duration: 0.5 ms
Velocity change: 15.4 ft/s
Waveform: Half-sin
C/C
NP0: Within ± 0.5% or 0.5 pF,
whichever is greater
X7R: ± 10%
D.F.
Within initial specified value
IR
Within initial specified value
Vibration
AEC-Q200
14
5 gs for 20 minutes, 12 cycles each of 3 orientations.
Note:
Use 8 x 5 PCB. 0.31 thick 7 secure points on one long side
and 2 secure points at corners of opposite sides. Parts
mounted within 2 from any secure point. Test from
10-2000 Hz.
C/C
NP0: Within ± 0.5% or 0.5 pF,
whichever is greater
X7R: ± 10%
D.F: meet initial specified value
IR meet initial specified value
购买、咨询产品请填写询价信息:(3分钟左右您将得到回复)
询价型号*数量*批号封装品牌其它要求
删除
删除
删除
删除
删除
增加行数
  • *联系人:
  • *邮箱:
  •  QQ:
  • *电话:

  • 关注官方微信

  • 联系我们
  • 电话:13714778017
  • 周一至周六:9:00-:18:00
  • 在线客服:

天天IC网由深圳市四方好讯科技有限公司独家运营

天天IC网 ( www.ttic.cc ) 版权所有©2014-2021 粤ICP备15059004号